304
رتبة | C | سيطر | مين | P | S | ني | Cr | مو |
201 | ≤0.15. | ≤0.75. | 5.5-7.5. | ≤0.06. | ≤ 0.03. | 3.5-5.5. | 16.0-18.0. | - |
301 | ≤0.15. | ≤1.0 | 2.0. | ≤0.045. | ≤ 0.03. | 6.0-8.0. | 16.0-18.0. | - |
304 | 0.08. | ≤1.0. | 2.0. | ≤0.045. | ≤ 0.03. | 8.0-10.5. | 18.0-20.0. | - |
304L | ≤0.03. | ≤1.0. | 2.0. | ≤0.035. | ≤ 0.03. | 9.0-13.0. | 18.0-20.0. | - |
316 | 0.08. | ≤1.0 | 2.0. | ≤0.045. | ≤ 0.03. | 10.0-14.0 | 16.0-18.0. | 2.0-3.0. |
316L | ≤0.03. | ≤1.0 | 2.0. | ≤0.045. | ≤ 0.03. | 12.0-15.0. | 16 .0-1 8.0. | 2.0-3.0. |
321 | 0.08. | ≤1.0 | 2.0. | ≤0.035. | ≤ 0.03. | 9.013 | 17.0-1 9.0. | - |
410 | ≤0.15. | ≤1.0 | ≤1.0. | ≤0.035. | ≤ 0.03. | - | 11.5-13.5. | - |
430 | ≤0.12. | ≤0.75. | ≤1.0. | ≤0.040. | ≤ 0.03. | ≤0.60. | 16.0-18.0. | - |
رتبة | C | سيطر | مين | P | S | ني | Cr | مو |
201 | ≤0.15. | ≤0.75. | 5.5-7.5. | ≤0.06. | ≤ 0.03. | 3.5-5.5. | 16.0-18.0. | - |
301 | ≤0.15. | ≤1.0 | 2.0. | ≤0.045. | ≤ 0.03. | 6.0-8.0. | 16.0-18.0. | - |
304 | 0.08. | ≤1.0. | 2.0. | ≤0.045. | ≤ 0.03. | 8.0-10.5. | 18.0-20.0. | - |
304L | ≤0.03. | ≤1.0. | 2.0. | ≤0.035. | ≤ 0.03. | 9.0-13.0. | 18.0-20.0. | - |
316 | 0.08. | ≤1.0 | 2.0. | ≤0.045. | ≤ 0.03. | 10.0-14.0 | 16.0-18.0. | 2.0-3.0. |
316L | ≤0.03. | ≤1.0 | 2.0. | ≤0.045. | ≤ 0.03. | 12.0-15.0. | 16 .0-1 8.0. | 2.0-3.0. |
321 | 0.08. | ≤1.0 | 2.0. | ≤0.035. | ≤ 0.03. | 9.013 | 17.0-1 9.0. | - |
410 | ≤0.15. | ≤1.0 | ≤1.0. | ≤0.035. | ≤ 0.03. | - | 11.5-13.5. | - |
430 | ≤0.12. | ≤0.75. | ≤1.0. | ≤0.040. | ≤ 0.03. | ≤0.60. | 16.0-18.0. | - |